【Product name】Zinc Oxide Eugenol Cement (Polymer-Reinforced)

【Specification】Powder:10g/bottle,15g/bottle, 30g/bottle, 40g/bottle; Liquid: 10mL/bottle,15 mL/bottle, 20mL/bottle

【Ingredients】 Zinc Oxide Eugenol Cement (Polymer-Reinforced) powder   is white to yellow and is primarily composed of zinc oxide, zinc acetate, polymethyl methacrylate, and shaping agents;   The liquid is clove oil with slightly yellow to yellow in color.

【Application】 Root canal sealing, temporary sealing of dental crown and filling, and pulp capping.

【Certification】 ISO13485/ Free Sales Certificate

【Product properties】

● Low viscosity

● Irreversible chemical change

● Low dimensional change

● Adhere well to dental compound

【Storage conditions】Storage at temperature of 5°C to 30°C, avoid direct sunlight.

【Service life】Unopened for two years, please use out in one month after opening.

【Contraindications】Contraindicated in patients with allergies to components of this product.

【Special reminder】Do not swallow.

【Caution】

1. The mixed cement of   Zinc Oxide contains eugenol, avoid using resin-based restorative materials during repair.

2. Gloves, mask and protective goggles should be worn during the procedure.

3. In case of skin contact, wash the skin with soap and plenty of water. Seek medical attention if skin irritation occurs.

4. If contact with the eyes, immediately rinse with plenty of water for15 minutes, open the eyelids, and seek immediate medical attention if nessessary.

5. If swallowed, rinse the mouth with plenty of water and drink a substantial amount of water. Seek medical treatment.

【Package】

Powder, 10g/ bottle               15g/ bottle               30g/ bottle               40g/ bottle	2 bottles x 1 box
Liquid,   10ml/   bottle               15ml/ bottle               20ml/ bottle

【How to use】

1.Place the powder and clove oil on a glass lab, with the recommended powder-to-liquid (P/L) weight ratio 1.8 : 3(g/g).

2. Mix the powder with the clove oil in three portions to obtain an uniform paste. Half of the powder should be mixed during the first round of mixing, and the remaining powder should be mixed in two additional rounds. Mix thoroughly within 3-4 minutes after the initial mixing.

3. The setting time of the mixed paste is relatively slow in cool, dry environments or with a low powder-to-liquid ratio. In warm, humid environments or with a high powder-to-liquid ratio, the setting time is faster. The curing time is approximately 10-15 minutes.